Hard tissue formation adjacent to implants of various size and configuration immediately placed into extraction sockets: an experimental study in dogs

Objectives To evaluate the influence of implant size and configuration on osseointegration in implants immediately placed into extraction sockets. Material and methods Implants were installed immediately into extraction sockets in the mandibles of six Labrador dogs. In the control sites, cylindrical transmucosal implants (3.3 mm diameter) were installed, while in the test sites, larger and conical (root formed, 5 mm diameter) implants were installed. After 4 months of healing, the resorptive patterns of the alveolar crest were evaluated histomorphometrically. Results With one exception, all implants were integrated in mineralized bone, mainly composed of mature lamellar bone. The alveolar crest underwent resorption at the control as well as at the test implants. This resorption was more pronounced at the buccal aspects and significantly greater at the test (2.7 +/- 0.4 mm) than at the control implants (1.5 +/- 0.6 mm). However, the control implants were associated with residual defects that were deeper at the lingual than at the buccal aspects, while these defects were virtually absent at test implants. Conclusions The installment of root formed wide implants immediately into extraction sockets will not prevent the resorption of the alveolar crest. In contrast, this resorption is more marked both at the buccal and lingual aspects of root formed wide than at standard cylindrical implants. To cite this article:Caneva M, Salata LA, de Souza SS, Bressan E, Botticelli D, Lang NP. Hard tissue formation adjacent to implants of various size and configuration immediately placed into extraction sockets: an experimental study in dogs.Clin. Oral Impl. Res. 21, 2010; 885-895.doi: 10.1111/j.1600-0501.2010.01931.x.

The Bone Formation Capabilities of the Anorganic Bone Matrix-Synthetic Cell-Binding Peptide 15 Grafts in an Animal Periodontal Model: A Histologic and Histomorphometric Study in Dogs

Background: The aim of this study is to verify the regenerative potential of particulate anorganic bone matrix synthetic peptide-15 (ABM-P-15) in class III furcation defects associated or not with expanded polytetrafluoroethylene membranes. Methods: Class III furcation defects were produced in the mandibular premolars (P2, P3, and P4) of six dogs and filled with impression material. The membranes and the bone grafts were inserted into P3 and P4, which were randomized to form the test and control groups, respectively; P2 was the negative control group. The animals were sacrificed 3 months post-treatment. Results: Histologically, the complete closure of class III furcation defects was not observed in any of the groups. Partial periodontal regeneration with similar morphologic characteristics among the groups was observed, however, through the formation of new cementum, periodontal ligament, and bone above the notch. Histologic analysis showed granules from the bone graft surrounded by immature bone matrix and encircled by newly formed tissue in the test group. The new bone formation area found in the negative control group was 2.28 +/- 2.49 mm(2) and in the test group it was 6.52 +/- 5.69 mm(2), which showed statistically significant differences for these groups considering this parameter (Friedman test P <0.05). There was no statistically significant difference among the negative control, control, and test groups for the other parameters. Conclusions: The regenerative potential of ABM-P-15 was demonstrated through new bone formation circumscribing and above the graft particles. The new bone also was accompanied by the formation of new cementum and periodontal ligament fibers. J Periodontol 2010;81:594-603.